ESTUDO COMPARATIVO DA CONFORMABILIDADE E DA RESISTÊNCIA À CORROSÃO DE ELETRODEPÓSITOS DE ZINCO OBTIDOS EM BANHO DE CLORETO COM ADITIVOS E EM BANHO DE SULFATO/CLORETO SEM ADITIVOS. PARTE 2: RESISTÊNCIA À CORROSÃO DOS REVESTIMENTOS

COMPARATIVE STUDY OF THE CORROSION RESISTANCE OF ZINC ELECTRODEPOSITS OBTAINED IN CHLORIDE BATH WITH ADDITIVES AND IN SULFATE/CHLORIDE BATH WITHOUT ADDITIVES PART 2: CORROSION RESISTANCE OF THE ELECTRODEPOSITS

Santos, Fabiano Raymundo dos; Panossian, Zehbour

Downloads: 1
Views: 1084

Resumo

Este artigo é a segunda parte do trabalho cujo objetivo é comparar as características, a conformabilidade e a resistência à corrosão de revestimentos de zinco produzidos por eletrodeposição em banho à base de cloreto com aditivos e em banho à base de sulfato/cloreto sem aditivos. A primeira parte apresentou a metodologia e os resultados dos ensaios de caracterização e de conformabilidade dos revestimentos. Esta apresenta a metodologia e os resultados dos ensaios de imersão em solução de cloreto de sódio e dos ensaios acelerados de corrosão (câmara de névoa salina e câmara úmida). Foi verificado que o revestimento obtido em banho de sulfato/cloreto sem aditivos apresenta maior resistência à corrosão do que o revestimento obtido em banho de cloreto com aditivos. A superioridade desse último foi atribuída à textura do zinco e à ausência de tensões residuais no eletrodepósito.

Palavras-chave

Eletrodeposição, Corrosão, Zinco, Textura.

Abstract

This paper is the second part of the work whose purpose is to compare the characteristics, formability and corrosion resistance of zinc coatings produced by electroplating in a chloride-based bath with additives and a sulfate/chloride bath without additives. The first part presented the methodology and the results of the characterization tests and of the formability tests. This part presents the methodology and the results of the immersion tests in a sodium chloride solution and of two corrosion accelerated tests (salt spray and humidity). The obtained results showed that the coating obtained from an additive-free sulfate/chloride bath has increased corrosion resistance more than the coating obtained from a chloride bath with additives. The superiority of the former was related to the texture of the zinc and the absence of residual stresses in the coating

Keywords

Electrodeposition, Corrosion, Zinc, Texture

Referências

1 Park H, Szpunar JA. The role of texture and morphology in optimizing the corrosion resistance of zinc-based electrogalvanized coatings. Corrosion Science. 1998;40(4-5):525-545.

2 Ashton RF, Hepworth MT. Effect of crystal orientation on the anodic polarization and passivity of zinc. Corrosion. 1968;24(2):50-53.

3 Dini JW. Electrodeposition: the materials science of coatings and substrates. Saddle River: Noyes Publications; 1993. 367 p.

4 Santos FR, Panossian Z. Estudo comparativo da conformabilidade e da resistência à corrosão de eletrodepósitos de zinco obtidos em banho de cloreto com aditivos e em banho de sulfato/cloreto sem aditivos: parte 1. Tecnologia em Materiais e Mineração. No prelo.

5 American Society for Testing and Materials. G1: standard practice for preparing, cleaning, and evaluating corrosion test specimens. West Conshohocken: ASTM; 2011. 9 p.

6 Associação Brasileira de Normas Técnicas. NBR 8094: material metálico revestido e não revestido corrosão por exposição à névoa salina. Rio de Janeiro: ABNT; 1983. 6 p.

7 Associação Brasileira de Normas Técnicas. NBR 8095: material metálico revestido e não revestido - corrosão por exposição à atmosfera úmida saturada: método de ensaio. Rio de Janeiro: ABNT; 2015. 3 p.

8 Panossian Z. Corrosão e proteção contra a corrosão de equipamentos e estruturas metálicas. São Paulo: IPT; 1993. 280 p. vol. 1.

5b8042380e88258440896e52 tmm Articles
Links & Downloads

Tecnol. Metal. Mater. Min.

Share this page
Page Sections