CHARACTERIZATION OF THE FRICTION CONDITIONS IN THE FINISHING STANDS OF A HOT STRIP MILL

CARACTERIZAÇÃO DAS CONDIÇÕES DE FRICÇÃO NO TREM ACABADOR DE UM LAMINADOR DE TIRAS A QUENTE

Gorni, Antonio Augusto; Silva, Marcos Roberto S. da

Downloads: 0
Views: 411

Abstract

The decrease in hot strength or even rolling load as strain increases in some stands of the finishing hot strip mill with no metallurgical reasons is a relatively common event. Apparently this fact is associated with modification in the tribological conditions between rolling stock and work roll surfaces due to unexpected interactions with scale. The aim of this work is to determine the values of the friction coefficient in the several stands of the finishing hot strip mill at Usiminas-Cubatão, as well to determine quantitative relationships between this coefficient and relevant process parameters, like strain degree and peripherical work roll speed.

Keywords

Hot strip rolling, Friction coefficient, Forward slip

Resumo

Não é raro observar redução na resistência à deformação ou mesmo na carga sob níveis crescentes de deformação em algumas cadeiras do trem acabador do laminador de tiras a quente sem que haja razões metalúrgicas para o fato. Aparentemente esse fato está associado à modificação das condições de atrito no arco de contato decorrentes de interações inesperadas com a carepa. Este trabalho tem como objetivo determinar os valores de coeficiente de atrito no trem acabador do laminador de tiras a quente da Usiminas-Cubatão. Além disso, são determinadas relações quantitativas entre esse coeficiente e parâmetros relevantes de processo, tais como grau de deformação e velocidade periférica dos cilindros de trabalho.

Palavras-chave

Laminação de tiras a quente, Coeficiente de atrito, Deslizamento a vante

Referências

1 GORNI, A. A.; SILVEIRA, J. H. D. Caracterização da ocorrência de recristalização dinâmica na laminação de tiras a quente. In: CONGRESSO ANUAL DA ABM, 60., 2005, Belo Horizonte, MG. Anais… São Paulo: ABM, 2005. p. 192-9.

2 WIESINGER, H. et al. Das kontinuierliche Stranggieβen und –walzen von Dünnbrammen. Stahl und Eisen, v. 110, n. 11, p. 81-8, Nov. 1990.

3 KOST, R. et al. Berechnung der Werkstoffkennwerte von Warbreitband auf Basis einer Walzspaltanalyse. Stahl und Eisen, v. 112, n. 11, p. 69-74, Nov. 1992.

4 REIMER, C.; HUISMAN, R. L. Geometrical effects of large reductions in first stands of finishing mill. Ironmaking and Steelmaking, v. 20, n. 4, p. 275-9, 1993.

5 MORALES, J. et al. Influence of process parameters on friction coefficient of high-chromium rolls. AISE Steel Technology, v. 76, n. 11, p. 46-48, Nov. 1999.

6 LI, Y. et al. Roll force model for online application in hot strip rolling with varying friction conditions. In: INTERNATIONAL CONFERENCE ON STEEL ROLLING, 9., 2006, Paris. Proceedings… Paris: Association Technique de la Siderurgie Française, 2006.

7 TSELIKOV, A. Stress and strain in metal rolling. Moscow: MIR, 1967.

8 MACCAGNO, T. M. et al. Determination of Tnr from rolling mill logs: comparison with laboratory data. ISIJ International, v. 34, n. 11, p. 917-22, Nov. 1994. http://dx.doi.org/10.2355/isijinternational.34.917

9 FLETCHER, A. J. et al. Prediction of roll force and torque during hot flat rolling of En2 steel. Metals Technology, v. 11, n. 4, 156-66, Apr. 1984.

10 SEREGIN, S. A. About mechanism of forward flow formation in rolling. Steel in Translation, v. 23, n. 4, p. 31-33, Apr. 1993.

588696997f8c9dd9008b45ef tmm Articles
Links & Downloads

Tecnol. Metal. Mater. Min.

Share this page
Page Sections