ESTUDO MICROESTRUTURAL DA ESCÓRIA DE CONVERTEDOR LD E SUA RELAÇÃO COM O PROCESSO DE DESFOSFORAÇÃO
MICROSTRUCTURAL STUDY OF THE LD CONVERTER SLAG AND ITS RELATIONSHIP TO THE DEPHOSPHORISATION PROCESS
Gonçalves, Hugo Filipe P.; Carneiro, Carlos André R.; Araújo, Túlio Carvalho da S.
http://dx.doi.org/10.4322/tmm.2014.006
Tecnol. Metal. Mater. Min., vol.11, n1, p.41-49, 2014
Resumo
A escória de convertedor LD desempenha papel fundamental no refino do aço, principalmente na remoção do fósforo. Muito se sabe sobre as caracterÃsticas fÃsico-quÃmicas da escória e sua relação com a eficiência do processo de refino, porém poucos utilizam o aspecto microestrutural para tal análise. Neste sentido, este trabalho teve como objetivo analisar a microestrutura da escória formada nos convertedores da Usiminas e compreender aspectos importantes relacionados à reação de desfosforação, para atuar de maneira efetiva na melhoria do processo industrial. Foi verificado que a reação de desfosforação não ocorre junto à s fases sólidas da escória. De acordo com estas observações, a quantidade de fundentes adicionada ao convertedor foi revista, alcançando-se uma expressiva redução no teor de CaO livre das escórias. Foi possÃvel observar, também, uma redução de 10% no consumo de cal carregado nos convertedores, sem interferir no teor médio de fósforo do aço ao fim de sopro.
Palavras-chave
Escória de convertedor, CaO livre, Microestrutura, Desfosforação
Abstract
The LD converter slag plays an important role in the refining process, mainly in relationship to phosphorus removal. Much is known about the physicochemical characteristics of the slag and its relationship to the process efficiency; however few employ the microstructural aspect for such analysis. In this sense, the aim of this work was to analyze the slag microstructure formed at Usiminas converters and to understand important points relationed to dephosphorisation reaction, to act efficiently in the industrial process improvement. It was verified that dephosphorisation reaction does not occur in slag solid phases. According to this observation, the amount of fluxes added to the converter was reviewed, reaching a considerable reduction in the free CaO content of the slags. It was also observed a drop of approximately 10% in lime consumption at the converters, without influence in the mean phosphorus content at the end of oxygen blown.
Keywords
Converter slag, Free CaO, Microstructure, Dephosphorization
Referências
1. Chang K-L, Huang C-T, Huang W-J, Liu Y-C. Investigations of microstructure and phosphorus distribution in BOF slag. China Steel Technical Report. 2008;(21):1-6.
2. Monaco A, Lu W-K. The properties of steel slag aggregates and their dependence on melt shop pratices. In: Proceedings of the 55th Ironmaking Conference Proceedings; 1996; Pittsburgh, EUA. Warrendale: Iron and Steel Society; 1996. p. 705-715.
3. Tossavainen M, Engstrom F, Yang Q, Menad N, Lidstrom M, Bjorkman B. Characteristcs of steel slag under different cooling conditions. Waste Management. 2007;27:1335-44. PMid:17005388. http://dx.doi.org/10.1016/j. wasman.2006.08.002
4. Inoue R, Suito H. Phosphorus partition between 2CaO.SiO2 particles and CaO-SiO2-FeO slags. ISIJ International. 2006;46(2):174-79. http://dx.doi.org/10.2355/isijinternational.46.174
5. Basu S, Lahiri A-K, Seetharaman S. Distribution of phosphorus and oxygen between liquid steel and basic oxygen steelmaking slag. Revue de Métallurgie. 2009;106(1):21-26. http://dx.doi.org/10.1051/metal/2009010
Facebook
Google+
Twitter
LinkedIn
Mendeley
StumbleUpon
CiteULike
Reddit
Email